Stainless Steel Electropolished Pipe
A554 Mirror Finish SS Tubing manufacturers in India
Stainless Steel Electropolished Pipe
A554 Mirror Finish SS Tubing
High Tensile Stainless Steel Pipes
High quality durable High Tensile SS Electropolished Pipes Stockist in India
Table of Content
- Specification Table of Stainless Steel Electropolished Pipe
- Most Common types A554 Mirror Finish SS Tubing
- Chemical Properties of High Tensile Stainless Steel Pipes
- Mechanical Strength Table of SS Mirror Finish Tubing
- Equivalent Material of Ferratic SS Electropolished Pipe
- Advantages of Electropolished SS Tubing
- Electropolished Stainless Steel Tube Dimensional Tolerances
- Temperature Range of ASTM A554 Polished SS Pipes
- Stainless Steel Mirror Pipe Surface finish
Specification Table of Stainless Steel Electropolished Pipe
| Specifications | ASTM A249, A269, A270 |
| Size | 1/8” NB to 24” NB, 1/4” OD to 24” OD sizes stainless steel welded tubes also available |
| Outer Diameter | 1/4" to 6" (6.35-165.2mm) |
| Wall Thickness | 0.4mm upto client requirement |
| Length | Up to 6 meters, custom cut lengths |
| Type | Seamless, Welded, Bright Annealed, Mechanically Polished, Electropolished, Semi Welded |
| Finish | BA Finish inside and outside, Electropolished finish inside and outside |
Most Common types A554 Mirror Finish SS Tubing
Stainless Steel Electropolished Tube
Electropolished Stainless Steel Tubing
Stainless Steel Mirror Pipe
Stainless steel polished Tubes
ASTM A554 Polished Stainless Steel Pipes
Electropolished Stainless Steel Tube
Mirror Finish Stainless steel Tubes
Electropolished SS Tubing
Chemical Properties of High Tensile Stainless Steel Pipes
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Ti | Fe | |
| 304 | min. | 18.0 | 8.0 | |||||||||
| max. | 0.08 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | 0.10 | ||||
| 304L | min. | 18.0 | 8.0 | |||||||||
| max. | 0.030 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 12.0 | 0.10 | ||||
| 304H | min. | 0.04 | 18.0 | 8.0 | ||||||||
| max. | 0.010 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | |||||
| SS 310 | 0.015 max | 2 max | 0.015 max | 0.020 max | 0.015 max | 24.00 26.00 | 0.10 max | 19.00 21.00 | 54.7 min | |||
| SS 310S | 0.08 max | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 0.75 max | 19.00 21.00 | 53.095 min | |||
| SS 310H | 0.04 0.10 | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 19.00 21.00 | 53.885 min | ||||
| 316 | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316L | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316TI | 0.08 max | 10.00 14.00 | 2.0 max | 0.045 max | 0.030 max | 16.00 18.00 | 0.75 max | 2.00 3.00 | ||||
| 317 | 0.08 max | 2 max | 1 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 57.845 min | ||||
| SS 317L | 0.035 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 11.00 15.00 | 57.89 min | |||
| SS 321 | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 5(C+N) 0.70 max | |||
| SS 321H | 0.04 0.10 | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 4(C+N) 0.70 max | |||
| 347/ 347H | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 20.00 | 9.0013.00 | |||||
| 410 | min. | 11.5 | ||||||||||
| max. | 0.15 | 1.0 | 1.00 | 0.040 | 0.030 | 13.5 | 0.75 | |||||
| 446 | min. | 23.0 | 0.10 | |||||||||
| max. | 0.2 | 1.5 | 0.75 | 0.040 | 0.030 | 30.0 | 0.50 | 0.25 | ||||
| 904L | min. | 19.0 | 4.00 | 23.00 | 0.10 | |||||||
| max. | 0.20 | 2.00 | 1.00 | 0.045 | 0.035 | 23.0 | 5.00 | 28.00 | 0.25 | |||
Check Stainless steel polished Tubes price in India
Mechanical Strength Table of SS Mirror Finish Tubing
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 304/ 304L | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 304H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 40 % |
| 310 / 310S / 310H | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 40 % |
| 306/ 316H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 316L | 8.0 g/cm3 | 1399 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 317 | 7.9 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 321 | 8.0 g/cm3 | 1457 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 347 | 8.0 g/cm3 | 1454 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 904L | 7.95 g/cm3 | 1350 °C (2460 °F) | Psi 71000 , MPa 490 | Psi 32000 , MPa 220 | 35 % |
Equivalent Material of Ferratic SS Electropolished Pipe
| STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
| SS 304 | 1.4301 | S30400 | SUS 304 | 304S31 | 08Х18Н10 | Z7CN18‐09 | X5CrNi18-10 |
| SS 304L | 1.4306 / 1.4307 | S30403 | SUS 304L | 3304S11 | 03Х18Н11 | Z3CN18‐10 | X2CrNi18-9 / X2CrNi19-11 |
| SS 304H | 1.4301 | S30409 | – | – | – | – | – |
| SS 310 | 1.4841 | S31000 | SUS 310 | 310S24 | 20Ch25N20S2 | – | X15CrNi25-20 |
| SS 310S | 1.4845 | S31008 | SUS 310S | 310S16 | 20Ch23N18 | – | X8CrNi25-21 |
| SS 310H | – | S31009 | – | – | – | – | – |
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | – | Z7CND17‐11‐02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
| SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
| SS 316H | 1.4401 | S31609 | – | – | – | – | – |
| SS 316Ti | 1.4571 | S31635 | SUS 316Ti | 320S31 | 08Ch17N13M2T | Z6CNDT17‐123 | X6CrNiMoTi17-12-2 |
| SS 317 | 1.4449 | S31700 | SUS 317 | – | – | – | – |
| SS 317L | 1.4438 | S31703 | SUS 317L | – | – | – | X2CrNiMo18-15-4 |
| SS 321 | 1.4541 | S32100 | SUS 321 | – | – | – | X6CrNiTi18-10 |
| SS 321H | 1.4878 | S32109 | SUS 321H | – | – | – | X12CrNiTi18-9 |
| SS 347 | 1.4550 | S34700 | SUS 347 | – | 08Ch18N12B | – | X6CrNiNb18-10 |
| SS 347H | 1.4961 | S34709 | SUS 347H | – | – | – | X6CrNiNb18-12 |
| SS 904L | 1.4539 | N08904 | SUS 904L | 904S13 | STS 317J5L | Z2 NCDU 25-20 | X1NiCrMoCu25-20-5 |
Mirror Finish Stainless steel Tubes Weight Chart
Advantages of Electropolished SS Tubing
- Better corrosion
- Smoothest finished, Mirror like finish
- Improved hygiene
- Improved product purity
- Enhance flow characteristics
Electropolished Stainless Steel Tube Dimensional Tolerances
| Size OD | Nominal Wall | Outside Diameter | Length | Wall |
|---|---|---|---|---|
| 1/2" (12.7) | 0.065" (1.65) | +/-0.005 (0.13) | +1/8" (3.18) - 0 | +/-10.0% |
| 3/4" (19.1) | 0.065" (1.65) | +/-0.005 (0.13) | +1/8" (3.18) - 0 | +/-10.0% |
| 1" (25.4) | 0.065" (1.65) | +/-0.005 (0.13) | +1/8" (3.18) - 0 | +/-10.0% |
| 1-1/2" (38.1) | 0.065" (1.65) | +/-0.008" (0.20) | +1/8" (3.18) - 0 | +/-10.0% |
| 2" (50.8) | 0.065" (1.65) | +/-0.008" (0.20) | +1/8" (3.18) - 0 | +/-10.0% |
| 2-1/2" (63.5) | 0.065" (1.65) | +/-0.010" (0.25) | +1/8" (3.18) - 0 | +/-10.0% |
| 3" (76.2) | 0.065" (1.65) | +/-0.010" (0.25) | +1/8" (3.18) - 0 | +/-10.0% |
| 4" (101.6) | 0.083" (2.11) | +/-0.015" (0.38) | +1/8" (3.18) - 0 | +/-10.0% |
| 6" (152.4) | 0.109" (2.77) | +/-0.030" (0.76) | +1" (25.4) -0 | +/-10.0% |
Temperature Range of ASTM A554 Polished SS Pipes
| Temperature Range | 1900°F (1040°C) |
View Electropolished Stainless Steel Tubing in Different Sizes
Stainless Steel Mirror Pipe Surface finish
| Surface finish | 15 µ-in Ra |